Wood bending test lab report
This mechanical testing method measures the behaviour of materials subjected to simple bending loads. Like tensile modulus, flexural modulus (stiffness) is calculated from the slope of the bending load vs. deflection curve. Flexural testing involves the bending of a material, rather than pushing or pulling, to determine the relationship between bending stress and deflection. Flexural testing is commonly used on brittle materials such as ceramics, stone, masonry and glasses. AbstractThe bending strength values of clearwood specimens are examined in the range of flexural fracture.
The values should be higher under centre loading than under third-point loading due to the size effect and decrease with increasing span length. The equations used for the size effect are criticised. The maximum tensile stress in the beams is lower for centre loading and higher for third-point loading, than calculated according to the classical beam theory. The purpose of the lab is to determine the Modulus of Elasticity, E, and the Shear Modulus, G for a given sample of wood. Using the Tinius Olson 5000 load frame, we will deflect two wood samples to collect load and deflection data.
With this data the modulus of elasticity and shear modulus can be found using deflection equations. Only one sample of wood will be tested to failure. Relevant TheoryDeflection in the beam for one point wood bending test lab report occurs at book report template 1st grade mid-span of a beam, since this is the point at which the moment is greatest.Note that the span distance, L, in the diagram is the support-to-support distance.
Description: In this lab experiment the mechanical properties of spruce wood specimens were determined. Five specimens were submitted to different tests. Two were tested for compression, one in parallel to the. In this lab experiment the mechanical properties of spruce wood specimens were determined. Two were tested for compression, one in parallel to the grain and the other perpendicular to it. One specimen was submitted to bending. The other two left were tested for tension, one in parallel to the grain and the other perpendicular to it. The tests gave wood bending test lab report loads and the respective deformations for each one of them.
Finally, the mode.